하이템프코리아 로고



하이템프코리아
Tel : 02-2663-1203  Fax : 02-2663-1204
서울 강서구 공항대로 190 푸리마 타워 617호
www.hightempkorea.com     hightempkorea@gmail.com

견적요청 바로가기

  • 에폭시 접착/코팅제
  • 세라믹 접착/코팅제
  • 세라믹 섬유
  • 세라믹 소재

A. 세라믹 소재

1. 알루미나(Alumina)

    - 튜브(Tube)

    - 열전대 보호관(한쪽 막힘)

    - 2홀 튜브(2 Hole tube)

    - 4홀 튜브(4 Hole tube)

    - 봉(Rod)

    - 각재(Bar)

    - 디스크(Disc)

    - 플레이트(Plate)

    - 도가니(Crucible)

------------------------------------

2. 마코(MACOR)

    - 봉재(Rod)

    - 각재(Square Bars)

    - 판재(Sheets)

------------------------------------

3. Shapal Hi M Soft™

    - 봉재(Rod)

    - 각재(Square Bars)

    - 판재(Sheets)

------------------------------------

4. High-End Ceramics

    - Aluminium Nitride(AlN)

    - Boron Nitride(BN)

    - Silicon Nitride(Si3N4)

     └ Tube, Rods

     └ Disc, Plates, nozzle

------------------------------------

5. 지르코니아(Zirconia)

    - 튜브(Tube)

    - 열전대 보호관(한쪽 막힘)

    - 도가니(Crucible)

    - 디스크(Disc)

    - 플레이트(Plate)

------------------------------------

6. 흑연(Graphite)

    - 흑연 도가니(Crucible)

------------------------------------

B. 세라믹 분말

    - 알루미나 파우더

    - BN 파우더

    - 실리카 파우더

    - Si3N4 파우더

    - TeO2 파우더

    - CeO2 폴리싱 파우더

BN 도가니(라이너) / Boron Nitride Crucible Liners

BN도가니/라이너

BN 도가니/라이너는(Boron Nitride Crucible Liners) 도가니의 손상을 최소화하며 고온에서 안정적이며 증발 속도와 수율이 우수합니다. 전력 효율이 우수하여 낮은 전력으로 더 높은 증발(증착) 속도를 달성할 수 있습니다.

Volume "A" Top Diameter "B" Bottom Diameter "H" Height Wall Thickness
7cc 29.46mm 22.1mm 14.22mm 2.36mm
10cc 32.51mm 22.1mm 19.05mm 2.36mm
15cc 37.59mm 28.45mm 17.27mm 3.18mm
25cc 44.45mm 33.02mm 21.08mm 2.36mm
40cc 50.8mm 37.85mm 26.92mm 6.35mm
75cc 63.5mm 46.48mm 31.75mm 6.35mm
100cc 69.85mm 51.05mm 35.05mm 0mm
BN도가니/라이너

Boron Nitride (BN) Property Data Sheet
Material
Properties
Units of
Measure
HBN HBR HBC HBT
Boron % >95 >94 >99 >99
Binder   Boric Acid Calcium Borate None None
Binder Melting Point ℃ 550 1150 --- ---
Max Operating Temperature Oxidizing Atmos. ℃ Vacuum Atmos. ℃ 550-580
1,150-1,600
850
1,150-1,600
850
2,000-3,000
850
2,000-3,000
Density Min/typical g/cc 2.00/2.10 1.90/2.00 1.90/1.95 1.70/1.75
Porosity % 7 11 13 22
Hardness Knoops(KHN, 100g) 19 26 16 11
Thermal Sh℃k Resistance T >1500℃ >1500℃ >1500℃ >1500℃
Specific Heat
     @ 25℃
     @ 700℃
J/Kg oK (Cal/g ℃) (808/.193)
1,846 (.411)
(808/.193)
1,846 (.411)
(808/.193)
1,846 (.411)
808(.193)
1,846 (.411)
Dielectric Strength V/mm x 103 53 53 54 34
Dielectric Constant @ 1GHz
@ 9.3 GHz
@ 1 MHz
4.3
4.4
4.2
4.2
4.3
4.1
4.1
4.3
4.1
3.9
3.9
3.8
Loss Tangent @1 GHZ
@ 9.3 GHz
@ 1 MHZ
.0003
.0002
<.0002
.0003
.0002
<.0002
.0004
<.0002
<.0002
.0003
<.0002
<.0002
Volume Resistivity @ 25℃
@ 700℃
>1015
108
>1015
108
>1015
1010
>1015
1010
Thermal Conductivity W/m oK @ 25℃
W/m oK @ 700 ℃
33
25
33
25
23
0.8
19
0.1
Coefficient. Thermal Expasion in per in/℃ x 10-6
(25℃ to 1,500℃)
6 3 0.8 0.1
Flexural Strength Mpa(psi x 103)
@25℃
Mpa(psi x 103)
@1,500℃

75.8

11

41.3

6

17.2

2.5

17.2

2.5
Modulus of Elasticity Gpa psi x 106 62.7 48.2 20.6 20.6
Compressive Strength Mpa psi x 103 124.1 62.0 51.7 38.6