Technical Properties
Property	Test	Result
Heat Resistance	Bending after heating. IEC 60684 Part 2 Clause13. 48 hours at 500°C	No cracking.
Flammability	Flame Propagation. IEC 60684 Part 2 Clause 26 Method B. Verticle with wire.	Will not ignite.
Cold Resistance	Bending at low temperature. IEC 60684 Part 2 Clause 14 at - 40°C	No cracking.
Chemical Resistance	Simulation of real operating conditions.	Excellent resistance to solvents. Compatible with most insulating varnishes.
Dielectric Strength
Test	Method	Minimum
IEC 60684	250 mm Inst. B/D Central Value (kV)	0.7
IEC 60684	250 mm Inst. B/D Lowest Value (kV)	0.6
UL 1441	25mm Inst. B/d (kV)	0.9

2. E 글라스 세라믹 슬리브/슬리빙 500℃

에어 필라멘트 화이버로 짜여진 "E" Glass 슬리브는 공기층을 가둠으로써 우수한 단열성능을 제공합니다.

- Air textured filament E Glass yarns
- 최대사용온도 550°C
- 불연성
- 복원성
- 가벼움

응용 분야
- 배기관 단열
- 라인 및 호스 단열

Basic Compositions of E Glass Fibre
SiO²	53-55%
Al²O³	14-15.5%
CaO -MgO	20-24%
B²O³	6.5-9%
Fe²O³	< 1%
Na²O-H²O	< 1%
General Properties of E Glass Fibre
Colour	White
Max Temperature	550°C
Melting Point	1200°C
Diameter Filaments	> 6-9 microns
Tensile Strength - Virgin Filament	3400 MPa
Young’s Modulus	7400 MPa
Thermal Conductivity	1.0 W/m °K
Fire Reaction	Incombustible
Loss on Ignition	< 1.5%
Dielectric Rigidity-glass in Bulk	60-100 KV/mm
Solvent Resistance	Good
Bases Resistance	Good
Acid Resistance	Good - except fluoridic acid.
General Properties of E Glass Fibre Textile Products
High Mechanical Strength	Good Electrical Properties
Incombustible	Good DimensionalStability
Low Thermal Conductivity	Good Resistance toChemicals Agents
High Thermal Resistance	Good Flexibility
Max Temperature	550°C

3. E 글라스 세라믹 우븐 슬리브/슬리빙 550°C(E Glass Woven Sleeving)

6-9μ 의 E glass 에어 텍스쳐 실로 직조되어 절연 및 단열성이 뛰어나며 직물구조로 단단하게 짜여 늘어나지 않습니다.

응용분야
- 전기케이블 전연/단열
- 파이프 및 호스 단열 용 단열전기 케이블
- 자동차 및 오토바이 배기관

Basic Compositions of E Glass Fibre
SiO²	53-55%
Al²O³	14-15.5%
CaO -MgO	20-24%
B²O³	6.5-9%
Fe²O³ - TiO²	< 1%
Na²O-H²O	< 1%
General Properties of E Glass Fibre
Colour	White
Max Temperature	550°C
Melting Point	1200°C
Diameter Filaments	> 6-9 microns
Tensile Strength - Virgin Filament	3400 MPa
Young’s Modulus	7400 MPa
Thermal Conductivity	1.0 W/m °K
Fire Reaction	Incombustible
Loss on Ignition	< 1.5%
Dielectric Rigidity-glass in Bulk	60-100 KV/mm
Solvent Resistance	Good
Bases Resistance	Good
Acid Resistance	Good - except fluoridic acid.
General Properties of E Glass Fibre Textile Products
High Mechanical Strength	Good Electrical Properties
Incombustible	Good Dimensional Stability
Low Thermal Conductivity	Good Resistance to Chemicals Agents
High Thermal Resistance	Good Flexibility
Max Temperature	550°C